Technical features:
Material: Polyolefin
Shrink Ratio: 3 : 1
Operating Temperature: – 55°C to 135°C
Shrink Temperature: > 100 °C
Burning behaviour: flame – retardent
Application: for wrapping of irregular shapes
| Test | Values | |
| Tensile strength | ISO 37 | > 10 MPa |
| Elongation at break | ISO 37 | > 250% |
| Specific weight | ISO 1183 | < 1,35 |
| Thermal shock | ASTM D2671 (4 h at 250°C) | no dripping, breaking or flowing |
| Heat aging Elongation at break |
ISO 188 (168 h at 175°C) ISO 37 |
> 150% |
| Flexibility at low temperature | ASTM D2671 (4h at -55°C) | no breaking |
| Flammability (exception transparent) | ASTM D876 | passed |
| Dielectric strength | IEC 243 | > 20 kV/mm |
| Corrosion resistance (copper contact and copper level) | ASTM D2671 | no corrosion |
| Water absorption | ISO 62 | < 0.5% |
Resistance to liquids
|
ISO 1817 ISO 37 |
|
| Resistance to fungi
Tensile strength |
ISO 846 |
|
Approvals:
| Military | UL | CSA |
| MIL-DTL 23053/5 DEF STAN 59-97 VG95343 Pt 5 |
UL 224 VW1 600 V, 125 ˚C |
600 V, 125 ˚C (OFTEN) |
Dimensions:
| Master number | min. diameter [mm] | max. diameter shrunk [mm] | Wall thickness after shrinkage [mm] | Roll length [m] |
| SSPO3S015 | 1,5 | 0,5 | 0,45 | 150 |
| SSPO3S030 | 3,0 | 1,0 | 0,55 | 150 |
| SSPO3S045 | 4,5 | 1,5 | 0,60 | 150 |
| SSPO3S060 | 6,0 | 2,0 | 0,65 | 75 |
| SSPO3S090 | 9,0 | 3,0 | 0,75 | 75 |
| SSPO3S120 | 12,0 | 4,0 | 0,75 | 75 |
| SSPO3S180 | 18,0 | 6,0 | 0,85 | 75 |
| SSPO3S240 | 24,0 | 8,0 | 1,00 | 30 |
| SSPO3S390 | 39,0 | 13,0 | 1,15 | 30 |
Standard color:
black (bw), other colors on request
Item number:
Example: SSPO3S015SW
SSPO3S015 = master number
SW = color black