Technical features:
| Test | Values | |
| Tensile strength | IEC 60684-2 paragraph 19.1 and 19.2 | > 35 MPa |
| Elongation at break | IEC 60684-2 paragraph 19.1 and 19.2 | > 150% |
| Thermal shock | IEC 60684-2 paragraph 6
(4h at 300 ˚C) |
No dripping, breaking or flowing of the outer wall |
| Heat aging
Tensile strength Elongation at break |
IEC 60684-2 paragraph 39
(168 h at 200 °C) paragraph 19.1 and 19.2 paragraph 19.1 and 19.2 |
>15 MPa > 75% |
| Corrosion resistance (copper mirror) | IEC 60684-2 paragraph 33 | no corrosion |
| Water absorption | IEC 60684-2 paragraph 40 | < 0.5% |
| Resistance to certain liquids
Tensile strength Elongation at break |
IEC 60684-2 paragraph 36 paragraph 19.1 and 19.2 |
excellent values > 25 MPa > 150% |
| Resistance to fungi
Tensile strength Elongation at break |
ISO 846 Method B IEC 60684-2 Paragraph 19.1 and 19.2 |
> 35 MPa > 150% |
Authorisations:
| Military | UL | CSA |
| MIL-DTL 23053/8 DEF STAN 59-97
VG95343 Pt 5 |
UL 224 VW1
600 V, 125 ˚C |
LR 31929
600 V, 125 ˚C (OFTEN) |
Dimensions:
| Master number | min. Diameter | max. Shrunk diameter | Wall thickness after shrinkage | Presentation | |||||
| Pieces | Rolls | ||||||||
| [mm] | [inches] | [mm] | [inches] | [mm] | [inches] | [m] | [m] | ||
| SSKY3/64″ | ♦ | 1,2 | 0.046 | 0,6 | 0.023 | 0,25 | 0.010 | 1,22 | 300 |
| SSKY1/16″ | ♦ | 1,6 | 0.063 | 0,8 | 0.031 | 0,25 | 0.010 | 1,22 | 300 |
| SSKY3/32″ | ♦ | 2,4 | 0.093 | 1,2 | 0.046 | 0,25 | 0.010 | 1,22 | 150 |
| SSKY1/8″ | ♦ | 3,2 | 0.125 | 1,6 | 0.062 | 0,25 | 0.010 | 1,22 | 150 |
| SSKY3/16″ | ♦ | 4,8 | 0.187 | 2,4 | 0.093 | 0,25 | 0.010 | 1,22 | 150 |
| SSKY1/4″ | ♦ | 6,4 | 0.250 | 3,2 | 0.125 | 0,30 | 0.012 | 1,22 | 75 |
| SSKY3/8″ | ♦ | 9,5 | 0.375 | 4,8 | 0.187 | 0,30 | 0.012 | 1,22 | 75 |
| SSKY1/2″ | ♦ | 12,7 | 0.500 | 6,4 | 0.250 | 0,30 | 0.012 | 1,22 | 75 |
| SSKY3/4″ | ♦ | 19,1 | 0.750 | 9,5 | 0.375 | 0,43 | 0.017 | 1,22 | 60 |
| SSKY1″ | ♦ | 25,4 | 1.000 | 12,7 | 0.500 | 0,48 | 0.019 | 1,22 | 60 |
♦ on request
Standard color:
transparent (tr)